Specifications

SKI-3S cis-isoprene synthetic rubber is cis-1,4-polyisoprene obtained by polymerization of isoprene in solution using stereospecific catalyst based on titanium. The rubber is stabilized by mixture of two non-staining antioxidants.
Content of cis-1,4-units, min: 96 %.
CAS: # 9003-31-0
REACH: registered
Application: for manufacture of auto tyres for lining of side-frames as well as coloured bicycle and motorcycle tyres, and also in manufacture of colored rubber goods, non-coloured industrial rubber goods used in manufacturing industry (rubber hoses, tubes, shoe soles). Rubber should not contain any foreign impurities and must meet the following requirements
Appearance: briquettes (bales)
Weight: 30.0+/-1.0 kg
Colour: from white to light-milky
Specific gravity: 0.91-0.92 g/cm3

Technical Requirements:

ParameterStandardTest Method
Mooney viscosity ML 1+4 (100°C)*72-88ASTM D 1646
Viscosity spread within a batch, units, max*5 
Volatile matter content, %, max (1 hour)*0.8ASTM D  5668
Ash content, %, max*0.35ASTM D 5667

Stearic acid content. %*

0.5-1.5Method used in the Russian Federation
Mixture of antioxidants:  
Agidol-1 (ВНТ) content, %*0.15-0.40Method used in the Russian Federation

Tris (2,4-di-tert-butylphenyl) phosphite content, %*

0.04-0.20

Method used in the Russian Federation
Rheometric PropertiesStandardTest Method
ML, dNm**1.0-2.0ASTM D 5289
MH, dNm**11.0-15.0ASTM D 5289
ts1, min**2.3-3.5ASTM D 5289
t’50, min**3.9-5.2ASTM D 5289
t’90, min**6.8-8.4ASTM D 5289

*  Specified in the certificate of quality.
** non rejectable.

Preparation of rubber mixes is carried out in accordance with ASTM D 3403-07, mixing – according to С method (on the roll mills). Roll mills are prepared according to ASTM D 3182-07. Vulcanization characteristics are determined according to ASTM D 5289 using an MDR 2000 rheometer (flow meter).Wait time for rubber mix before testing is 2-6 hours.

Rubber mix recipe and measurement conditions:

Rubber mix recipe in parts by weight!Standard
Rubber100.00
Zinc oxide5.00
IRB 7 (N330) carbon black35.00
Sulphur2.25
Stearic acid2.00
TBBS ( N-tert-Butyl-2-benzothiazolesulfenamide)0.70
Rheometer MDR 2000,measurement conditions:Standard
Temperature, °C160
Duration, min30
Oscillation amplitude, deg+/-0.5
Oscillation frequency, Hz1.7

Packaging:

Rubber briquettes (bales) are packaged in double-layer marked PE film (thickness of 0.05 +/- 0.01 mm, melting temperature of 108-112°C), then – in plastic box pallets of 540kg or in plywood or metal containers of 1,260kg.

Transportation:

Rubber is transported by all types of transport in covered transporting means in accordance to all rules of cargo’s transportation standing at transport of this form.

Storage:

Under normal conditions of storage (at a temperature not exceeding 30°C, in dry place free from direct sunlight)

Guaranteed Shelf Life:

2 (two) years from the manufacture date. After the expiration of the guaranteed shelf life, the rubber can be used for its intended purpose after confirmation of its conformity to the requirements of this product specification